14871-92-2, In the next few decades, the world population will flourish. As the population grows rapidly and people all over the world use more and more resources, all industries must consider their environmental impact.14871-92-2, (2,2¡ä-Bipyridine)dichloropalladium(II) it is a common compound, a new synthetic route is introduced below.
General procedure: [Pd(bpy)Cl2] (0.20 g, 0.60 mmol) was suspended in water (25 mL). Silver nitrate (0.20 g, 1.19 mmol) in water (5 mL) was added and the reaction mixture was stirred for 6 h at 60 C and then at room temperature, always in absence of light. The resulting solution was centrifuged and filtered to remove AgCl. A few drops of water, glycolic acid (0.05 g, 0.66 mmol) and 1 M NaOH (1.20 mL) were added to the filtrate. The resulting solution was stirred for 5 days and concentrated at 60 C to 5 mL on a rotary evaporator. The mixture was cooled to room temperature and the yellow powder was filtered off and dissolved from water and again concentrated to 5 mL. Yellow single crystals suitable for X-ray diffraction were obtained from the resulting solution by slow evaporation at room temperature.
This compound has a wide range of applications. It is believed that with the continuous development of the source of the synthetic route,14871-92-2,(2,2¡ä-Bipyridine)dichloropalladium(II),its application will become more common.
Reference£º
Article; Balboa, Susana; Carballo, Rosa; Castineiras, Alfonso; Gonzalez-Perez, Josefa Maria; Niclos-Gutierrez, Juan; Polyhedron; vol. 50; 1; (2013); p. 512 – 523;,
Chapter 1 An introduction to palladium catalysis
Palladium/carbon catalyst regeneration and mechanical application method